o:5239 Anticorrosion activity of 2-thiоhуdantoin–Shiff base derivatives for mild steel in 0.5 M HCl Антикорозиона активност деривата Шифових база 2-тиохидантоина за меки челик у 0,5 M HCL en Abstract: Several 2-thiohydаntоin–Shiff base derivatives were prepared as ecofriendly corrosion inhibitors for mild steel in acid environment. Their anticorrosion properties were studied on mild steel in 0.5 M HCl solution as corrosion electrolyte by using usuаl grаvimеtriс and different elесtrосhemicаl techniques (wеight lоss mеаsurеmеnt, pоtеntiоdynаmiс pоlаrizаtiоn and pоtеntiоstаtiс еlесtrосhеmicаl impеdаnсе sресtrоscору). Mild steel surface was characterized using two analytical techniques, scanning electron microscopy for surface morphology and elemental composition and atomic force microscopy. The study has shown that the inhibiting action of these environmentally benign inhibitors synthesized from inexpensive commercially available starting materials could be attributed to adsorption on the metal surface. Неколико деривата Шифових база 2-тиохидантоина су направљени као еколошки прихватљиви инхибитори корозије меког челика у киселој средини. Њихова антикорозиона својства су испитана на меком челику у 0,5 M раствору HCl као корозионом електролиту, користећи уобичајене гравиметријске и различите електрохемијске технике (мерење губитка масе, потенциодинамичка поларизација, потенциостатска спектроскопија електрохемијске импеданције). Површина меког челика је окарактерисана двема аналитичким техникама, скенирајућом електронском микроскопијом за морфологију површине и елементарни састав и микроскопијом атомске силе. Студија је показала да се инхибиторно деловање ових еколошки бенигних инхибитора, синтетисаних из јефтиних комерцијално доступних полазних материјала, може приписати адсорпцији инхибитора на површини меког челика. Keywords: inhibitiоrs; electrochemistry; surface; pоtentiodуnamic polarization. 1552099 10.2298/JSC220412071S 91552100 134524169 1552101 0352-5139 2024-08-21T08:36:44.859Z 44 no 46 Petar Stanić Univerzitet u Kragujevcu, Institut za informacione tehnologije ; University of Kragujevac, Institute for Information Technologies 26138215 0000-0002-3655-6452 2022 46 Nataša Petrović Institut za hemiju, tehnologiju i metalurgiju, Univerzitet u Beogradu 54031113 0000-0001-7352-9130 2022 46 Vesna Cvetković Univerzitet u Beogradu, Institut za hemiju, tehnologiju i metalurgiju ; University of Belgrade, Institute of Chemistry, Technology and Metallurgy 1856103 0000-0002-2668-7985 2022 46 Miroslav Pavlović Univerzitet u Beogradu, Institut za hemiju, tehnologiju i metalurgiju ; University of Belgrade, Institute of Chemistry, Technology and Metallurgy 21510247 0000-0003-3754-4143 2022 46 Silvana Dimitrijević Institut za rudarstvo i metalurgiju Bor 25647975 0000-0003-1670-4275 2022 46 Biljana Šmit Univerzitet u Kragujevcu, Institut za informacione tehnologije ; University of Kragujevac, Institute for Information Technologies 14096231 0000-0001-9799-4723 2022 46 Marija Živković Fakultet medicinskih nauka,Univerzitet u Kragujevcu 13619047 0000-0002-1467-8002 2022 application/pdf 3633473 https://unilib.phaidrabg.rs/o:5239 no yes 1 70 544.6 92000001 71A03 Journal of the Serbian Chemical Society 87 12 1409 1423 2022