o:3914 Investigation of Bi2Te2.88Se0.12 bulk single crystal produced using Bridgman method en Abstract: As part of research on the influence of selenium as dopant on bismuth telluride, a successful synthesis of single crystal was carried out. Single crystal of p type conductivity, with the given compound formula, Bi2Te2.88Se0.12, was obtained by the Bridgman process. The obtained empirical formula does not deviate from the given compound formula. Single crystal was characterized by Hall Effect system based on the Van der Pauw method. Also, bulk sample was characterized by Seebeck coefficient (S), thermal conductivity (κ) and electrical resistivity (ρ) measurements, as а function of temperature in the range of 40 - 320°C by а home made impedance meter. The prepared single crystal has a figure of merit (Z) of 2.16 x 10-3 K-1 at 40°C. Values of ZT are about 1.0 at 27°C for commercialized p and n type of bismuth telluride ingots. T is absolute temperature. Садржај: У оквиру истраживања утицаја селена као допанта на бизмут телурид, извршена је успешна синтеза монокристала. Монокристал п типа проводљивости, са датом формулом једињења, Bi2Te2.88Se0.12, добијен је Бриџмановим поступком. Добијена емпиријска формула није одступала од дате формуле једињења. Монокристал је окарактерисан системом Холовог ефекта заснованом на Ван дер Пауовој методи. Такође, масовни узорак је окарактерисан Зебековим коефицијентом (S), мерењима топлотне проводљивости (κ) и електричне отпорности (ρ) у функцији температуре у опсегу од 40 - 320°C мерачем импедансе домаће израде. Припремљени монокристал има висок фактор квалитета (Z) од 2.16 x 10-3 К-1 на 40°C. За комерцијализоване инготе бизмут телурида п и н типа вредности ZT су око 1.0 на 27°C. Т је апсолутна температура. Keywords: Bulk single crystal, Bridgman method, Hall and Van der Pauw method, Thermoelectric properties, Doping. Кључне речи: Масивни монокристал, Бриџман метода, Холова и Ван дер Паува метода, термоелектрична својства, допирање. 1552099 10.2298/SOS231017056P 91552100 136721673 1552101 1820-7413 2024-02-02T09:57:49.098Z 44 no 46 Emina Požega Institut za rudarstvo i metalurgiju Bor 0000-0001-6797-2435 Danjela Simonović Institut za rudarstvo i metalurgiju Bor person 0000-0001-7945-693X Anđela Stojić Tehnički fakultet u Boru person Igor Svrkota Institut za rudarstvo i metalurgiju Bor person 0000-0002-3779-6327 Ana Petrović Institut za rudarstvo i metalurgiju Bor person 0000-0002-9815-6884 Saša Marjanović Tehnički fakultet u Boru person 0000-0001-6930-2232 Slavko Bernik Jožef Stefan Institute, Ljubljana, Slovenia person application/pdf 893148 https://unilib.phaidrabg.rs/o:3914 no yes 16 70 92000001 71A03 Science of Sintering [Elektronski izvor] 56 00 1 15 2024